    • Electronic transport and magnetoresistivity of La0.4Bi0.1Ca0.5–𝑥Sr𝑥MnO3 (𝑥 = 0.1 and 0.2)

      P Subhashini B Munirathinam M Krishnaiah R Venkatesh D Venkateshwarlu V Ganesan

      More Details Abstract Fulltext PDF

      Electrical resistivity and magnetoresistive behaviour of bismuth-substituted lanthanum manganites La0.4Bi0.1Ca0.5–𝑥Sr𝑥MnO3 (𝑥 = 0.1 and 0.2) were systematically studied by varying the temperature from 2 to 300 K and the magnetic field up to 12 T. The samples were found to crystallize in rhombohedral structure and their morphology shows near-spherical nanosize crystallites. Charge ordering was observed in both the samples under zero field conditions and corresponding transition temperature 𝑇CO was found to decrease with the increase of 𝑥. Resistivity measurements with magnetic field also showed suppression of magnetoresistivity (MR) with the increase of 𝑥 and the maximum MR was found to be 98 and 93% for 𝑥 = 0.1 and 0.2, respectively, at 10 T. In the high-temperature domain, the electronic transport was observed to be dominated by the variable range hopping mechanism for both the samples, whereas in the low-temperature domain the electrical conduction of 𝑥 = 0.1 sample was observed to be contributed by various other electron scattering mechanisms.

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.