    • Synthesis and degradation properties of 𝛽-TCP/BG porous composite materials

      Fan Xin Chen Jian Ruan Jianming Zhou Zhongcheng Zou Jianpeng

      More Details Abstract Fulltext PDF

      𝛽-TCP/BG porous composite materials were successfully fabricated by foaming technology. X-ray diffraction was used to determine the crystal structure of powders. The pore size and distribution of the resulting materials were characterized using scanning electron microscopy. The porosity and degradation performance of materials were also investigated. The results showed that the porous composite materials possessed the pore size ranging from 100 to 500 𝜇m in diameter, whereas the interconnection among macrospores was poor. The porosity in materials increased from 58.7% to 63.47% with BG content ranging from 0 to 3 wt%, further increasing of BG content results in a decrease in porosity. The degradation rate of composite materials can be adjusted by varying the BG content.

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.