Volume 45 All articles Published: 18 November 2022 Article ID 0233
High pressure investigations on neutron irradiated ferroboron
ANAND KUMAR UTTYIOARNAB SAHA E RADHA K DEVAN N R SANJAY KUMAR C N VENKITESWARAN R DIVAKAR N V CHANDRA SHEKAR
This study reports the pressure effect on structural stability of neutron irradiated ferroboron systems. Ferroboron, a mixture of boron and iron, has been found to have three phases, i.e., FeB, Fe$_2$B and Fe$_3$B. Studies have been conducted on single-phase Fe$_2$B and ferroboron. Fe$_2$B adopts tetragonal structure at ambient and undergoes structural transition to orthorombhic phase at 6 GPa. Further, Fe2B is irradiated with neutrons with a fluence of ${\sim}$10$^{17}$ n cm$^{–2}$ and yields bulk modulus of 254 GPa, which is 16% enhancement as compared to unirradiated sample. The defects are estimated by the use of SRIM code. Total displacement per atom (dpa) in Fe$_2$B for the irradiation fluence is found to be 5.53${\times}$10$^{-5}$. The study also shows that phase transition seen in pristine Fe$_2$B is inhibited upon neutron irradiation under pressure up to 24 GPa. Similar result was obtained on ferroboron mixture, irradiated with a neutron fluence of 8.18${\times}$10$^{21}$ n cm$^{-2}$ with dpa of 2.8. The irradiated sample is found to be stable up to 16 GPa.
Volume 46 All articles Published: 28 February 2023 Article ID 0041 CORRECTION
Correction to ‘High pressure investigations on neutron irradiated ferroboron’
ANAND KUMAR UTTIYOARNAB SAHA E RADHA K DEVAN N R SANJAY KUMAR C N VENKITESWARAN R DIVAKAR N V CHANDRA SHEKAR
Volume 46, 2023
All articles
Continuous Article Publishing mode
Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
Chemical Sciences 2020
Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
Physical Sciences 2020
Click here for Editorial Note on CAP Mode
© 2023-2024 Indian Academy of Sciences, Bengaluru.