Volume 36 Issue 2 April 2013 pp 301-309
DTA and TGA curves of titanium hydride powder were determined in air at different heating rates. Also the thermal decomposition behaviour of the aforementioned powder at high heating rates was taken into consideration. A great breakthrough of the practical interest in the research was the depiction of the 𝑃H2-time curves of TiH2 powder at various temperatures in air. In accordance with the results, an increase in heating rate to higher degrees does not change the process of releasing hydrogen from titanium hydride powder, while switching it from internal diffusion to chemical reaction. At temperatures lower than 600 °C, following the diffusion of hydrogen and oxygen atoms in titanium lattice, thin layers TiH𝑥 phase and oxides form on the powder surface, controlling the process. On the contrary, from 700 °C later on, the process is controlled by oxidation of titanium hydride powder. In fact, the powder oxidation starts around 650 °C and may escalate following an increase in the heating rate too.
Volume 43, 2020
Continuous Article Publishing mode
Click here for Editorial Note on CAP Mode