    • Emulsion-based synthesis of NaA zeolite nanocrystals and its integration towards NaA membranes

      M K Naskar A Das D Kundu M Chatterjee

      More Details Abstract Fulltext PDF

      NaA zeolite nanoparticles (seed crystals) of size 50–65 nm were synthesized using water-in-oil (w/o) type emulsions at a considerably low temperature of 65 ± 1°C in a short duration of 2 h. The emulsions were stabilized using non-ionic surfactants e.g. sorbitan monooleate (Span 80), sorbitan monolaurate (Span 20), polyoxyethylene(5)nonylphenylether with ethoxy numbers of 5 (Igepal CO-520) and polyoxyethylene sorbitan monooleate (Tween 80) of hydrophilic-lipophilic balance (HLB) values of 4.3, 8.6, 10 and 15 respectively. Among the surfactants, the intermediate HLB values of 8.6 (Span 20) and 10 (Igepal CO-520) were effective in synthesizing highly dispersible NaA nanoparticles of size 50–65 nm. The membrane prepared hydrothermally in multi-steps at 65 ± 1°C, using the Span 20-derived seed crystals deposited on porous support, showed the formation of high quality interlocked NaA coating. Single gas nitrogen (N2) permeation of the membrane exhibited a permeance value of 1.01 × 10-8 mol m-2 s-1 Pa-1 at ambient temperature (30°C).

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.