    • Electrical properties and scaling behaviour of Sm3+ doped CaF2-bismuth borate glasses

      A A Ali M H Shaaban

      More Details Abstract Fulltext PDF

      The electrical properties for 20Bi2O3–60B2O3 (20−𝑥)–CaF2–𝑥Sm2O3 glasses (0 ≤ 𝑥 ≤ 2) were measured in the temperature range 297 K up to 629 K and in the frequency range 0.1–100 kHz. The d.c. and a.c. conductivity values and the dielectric loss (tan 𝛿) values were found to increase with increasing Sm2O3 content, whereas the activation energy of conductivities and the dielectric constant decreased. These results were attributed to the introduction of the rare earth ions; promote the formation of a high number of non-bridging oxygen atoms, which facilitate the mobility of charge carriers. The frequency dependence of the a.c. conductivity follows the power law 𝜎ac(𝜔) =A𝜔s . The frequency exponent (𝑠) values (0.64 < 𝑠 < 0.8) decrease with increasing temperature. This suggested that the a.c. conduction mechanism follows the correlated barrier hopping model (CBH). The dielectric constant (𝜀') and dielectric loss (tan 𝛿 values) were found to increase with increasing temperature and increasing Sm2O3 concentration in the glass. The a.c. conductivities as a function of frequency at different temperatures of a given glass superimposed onto a master curve (Roling scaling model). Furthermore, we have performed to scale the data as a function of composition. Two master curves were obtained, which suggested that there are differences in dominant charge carriers between glasses having Sm2O3 concentration ≥1 and glass of Sm2O3 concentration <1.

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.