    • Keywords

       

      Hydrogen storage; MmNi5 alloy; PCI curves; microstructure; thermodynamic.

    • Abstract

       

      The microstructures and thermodynamic properties of MmNi5-xAlx hydrogen storage alloys are studied in this article. The structure was assessed with XRD and SEM. Pressure-composition isotherms for hydrogen absorption/desorption at 0, 25 and 50 ̊C were used for assessment of thermodynamic properties. XRDresults show that the samples consist of single-phase CeNi5–type. The alloys exhibit second phases, porosities, and cracks. Al microsegregation is the main reason for the second phase formation. With increasing Al, the microsegregation and the amount of second phases are increased. The hydrogen storage capacities of MmNi5- xAlx (x = 0.2, 0.3, 0.4 at %) alloys are 1.40, 1.37 and 1.34 wt%, respectively. The equilibrium pressures and hysteresis (1.14, 0.96 and 0.72 for 0.2, 0.3 and 0.4 Al, respectively) for all three compositions decrease withincreasing Al, that proves the formation of more stable hydrides. Furthermore, the enthalpy of hydride formation decrease to -20.770, -23.565, -26.306 kJ mol-1 H2 for the MmNi5-xAlx (x = 0.2, 0.3, 0.4 at %) alloys, respectively. This shows the improvement of thermodynamic stability and properties.

    • Author Affiliations

       

      SEIFOLLAHI MASUMEH1 JOUDAKI MOHAMMAD1 MAHDI ABBASI SEYED1 MAHDI GHAZI MIR SAEED SEYED1

      1. Faculty of Materials & Manufacturing Technologies, Malek Ashtar University of Technology, Tehran, Iran
    • Dates

       
  • Sadhana | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.