• Elevated temperature molten salt corrosion study of SS304L austenitic boiler steel

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/sadh/045/0199

    • Keywords

       

      Hot corrosion; SEM/EDS; salt mixtures; XRD; high temperature oxidation; 304L stainless steel.

    • Abstract

       

      The aim of this study is to investigate the high-temperature corrosion behavior of 304L stainless steel in the environment of various molten salt mixtures in the temperature range of 550–850°C. Weight change measurement has been done and characterization of corroded specimen was carried out using XRD, SEM/EDStechniques. Findings indicate that high chloride concentration salts affect the corrosion resistance adversely. The protective behavior of Cr2O3 layer deteriorated and its passivation is hindered at higher temperature owing to thechlorination-oxidation process. Fe2O3 and (Fe, Cr)xOy were found to be the major phases in the corrosion product. The salts were found to significantly affect the corrosion of 304L stainless steel in the following order: K2SO4 + 60% NaCl>Na2SO4 + 50% NaCl>40% K2SO4 + 40% Na2SO4 + 10% KCl + 10%NaCl>Na2SO4 + 60% V2O5 >Air.

    • Author Affiliations

       

      SUMIT MAHAJAN1 RAHUL CHHIBBER

      1. Department of Mechanical Engineering, IIT Jodhpur, Jodhpur, Rajasthan 342037, India
    • Dates

       
  • Sadhana | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.