      Composites; thick films; positive up negative down measurements; polarisation; hysteresis; multiferroics.

    • Abstract

       

      $\rm{Ni–Co–Cu–Mn\,Ferrite+PZT (PbZr_{0.52}Ti_{0.48}O_{3})}$ ferroelectric: composite thick filmswere prepared by the screen-printing method. The normal XRD and the low glancing angle XRD confirm the presence of both phases in the composite thick films. Back-scattered SEM shows 0-3 and 3-3 types of connectivity. The magnetic ordering of the ferrite phase was confirmed from $M–H$ hysteresis loop whereas the electric ordering of the ferroelectric phase was confirmed from $P–E$ hysteresis curve. Various measurable parameters from the loop were studied as a function of the mole percent of constituent phases. PUND (positive up negative down) analysis was done to determine the resultant polarisation contributed by the participating phases in the composites. Dielectric and magnetoelectric (ME) measurements were analysed in the light of PUND measured data.

    • Author Affiliations

       

      P S JADHAV1 K K PATANKAR2 V L MATHE3 Y D KOLEKAR4 R C KAMBALE4 VIJAYA PURI5

      1. Department of Physics, R.B.N.B. College, Shrirampur 413 709, India
      2. Department of Physics, Rajaram Collage, Kolhapur 416 004, India
      3. Novel Materials Research Lab, Department of Physics, Savitribai Phule Pune University, Pune 411 007, India
      4. Multiferroic Research Lab, Department of Physics, Savitribai Phule Pune University, Pune 411 007, India
      5. Thick and Thin Films Research Lab, Department of Physics, Shivaji University, Kolhapur 416 004, India
    • Dates

       
  • Pramana – Journal of Physics | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.