    • Keywords

       

      Carbon nanotubes; thin films; chemical vapour deposition; scanning electron microscopy; Raman spectroscopy.

    • Abstract

       

      We report the influence of catalyst formulation and reaction temperature on the formation of carbon nanotube (CNT) thin films by the chemical vapour deposition (CVD) method. Thin films of CNTs were grown on Fe–Mo/Al2O3-coated silicon wafer by thermal decomposition of methane at different temperatures ranging from 800 to 1000°C. The electron microscopic investigations, SEM as well as HRTEM, of the as-grown CNT thin films revealed the growth of uniform multi-walled CNTs in abundance. The intensity ratio of D-band to G-band and FWHM of G-band through Raman measurements clearly indicated the dependency of structural defects and crystallinity of CNTs in thin films on the catalyst formulation and CVD growth temperature. The results suggest that thin films of multi-walled CNTs with negligible amount of defects in the nanotube structure and very high crystallinity can be obtained by thermal CVD process at $925^{\circ}$C.

    • Author Affiliations

       

      S S Mahajan1 M D Bambole1 S P Gokhale1 A B Gaikwad1

      1. Physical & Materials Chemistry Division, National Chemical Laboratory, Dr Homi Bhabha Road, Pune 411 008, India
    • Dates

       
  • Pramana – Journal of Physics | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.