      Bimetallic nano alloys; Mizoroki–Heck reaction; Suzuki coupling; Ni-Pd-ABPBI; Cu-Pd-ABPBI

    • Abstract

       

      Novel Ni-Pd and Cu-Pd bimetallic nano alloys was designed and heterogenized on the highly robust ABPBI [poly(2,5-benzimidazole)] polymer in high yields using NaBH4 as reducing agent. These were versatile ligand free catalysts for the Mizoroki–Heck reaction and Suzuki–Miyaura coupling. The bimetallic Ni-Pd-ABPBI catalyst for the Mizoroki–Heck reaction of 4-iodo anisole could be recycled 5 times with high yields. Aryl bromides could also be activated for the Mizoroki–Heck reaction using Cu-Pd-ABPBI NP catalysts, with moderate yields.

    • Graphical Abstract

       

      Synopsis Novel bimetallic Ni-Pd and Cu-Pd nano alloys, heterogenized on the robust ABPBI [poly(2,5-benzimidazole)] polymer using NaBH as reducing agent, is described. These were versatile ligand free, noble metal conservative catalysts, for the Mizoroki–Heck reaction and the Suzuki–Miyaura coupling. Aryl bromides were activated for the Mizoroki–Heck reaction using the Cu-Pd-ABPBI catalyst
    • Author Affiliations

       

      VIJAY P PATIL1 2 ABHIJIT A KASHID1 BHANUPRATAP S SOLANKI2 3 ULHAS K KHARUL4 3 SURESH IYER1 3

      1. Organic Chemistry Division, National Chemical Laboratory, Dr. Homi Bhabha Road, Pashan, Pune 411008, Maharashtra, India
      2. Chemical Engineering and Process Development, National Chemical Laboratory,Pashan, Pune 411008, Maharashtra, India
      3. Academy of Scientific and Innovative Research (AcSIR), New Delhi 110025, India
      4. Polymer Science and Engineering Division, National Chemical Laboratory, Dr. Homi Bhabha Road,Pashan, Pune 411008, Maharashtra, India
    • Dates

       
  • Journal of Chemical Sciences | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.