    • Keywords


      Nano-architecture; Ni-foam; Co& #8323; O& #8324; charge storage

    • Abstract


      Nanostructured Co₃O₄ on Ni-foam has been synthesized with diverse morphologies, high surface area and porosity by employing different surfactants under hydrothermal conditions and subsequent calcination. The surfactants strongly influence the physicochemical properties of cobalt oxide samples. The cobalt oxide grown on Ni-foam without surfactant had flower-like morphology. However, cobalt oxides synthesized by using cationic (CTAB) and non-ionic (Triton X-100) surfactants showed flake-like morphology, but the spatial arrangement of flakes was found to be different in both the samples. The surfactant-assisted cobalt oxide showed average crystallite size of ∼6.6–9.8 nm, surface area of 60–80 m2g−1 and porosity (pore diameter ∼3.8 nm). These samples were found to perform better as charge storage electrode materials. The specific capacitance values of cationic and non-ionic surfactant-assisted cobalt oxide materials, at a current density of1.0 A g−1, were 1820 and 806 F g−1, respectively, compared to 288 F g−1 of cobalt oxide prepared without surfactant. They also showed excellent capacity retention for over 3000 charge-discharge cycles at higher current densities. The difference in the capacitance values of cationic and non-ionic surfactant-assisted cobalt oxide is due to the difference in the flake arrangement.

    • Author Affiliations

    • Dates

    • Supplementary Material

  • Journal of Chemical Sciences | News

© 2021-2022 Indian Academy of Sciences, Bengaluru.