      Ag-doped lanthanum chromites; borohydride oxidation; perovskite; precursor complex; combustion route.

    • Abstract

       

      The electrocatalytic activity of Ag-doped lanthanum chromites electrode materials viz., LaCr0.4Ag0.6O3 and LaCr0.7Ag0.3O3 prepared by decomposing the precursor complex is studied. Pure LaCrO3 is synthesized by combustion route using oxalic acid as a fuel. The decomposition behaviour of the assynthesized powder obtained in the latter method is characterized by TGA-DTA and XRD. Both the precursor complex and the as-synthesized powder are calcined at 900°C for 7 and 10 h, respectively. XRD of the final product after calcinations indicated the formation of perovskite phase with minor amounts of impurity phases of component oxides in the Ag-doped lanthanum chromites and pure perovskite phase in the undoped one. The surface morphology of the perovskites is studied by SEM. The electrocatalytic activity of the perovskite powders for borohydride oxidation is studied by using cyclic voltammetry (CV) at a catalyst loading of 0.7 mgcm−2 for both Ag-doped and undoped LaCrO3 coated on glassy carbon substrate. Calibration plots are obtained by plotting the anodic peak current versus concentration of borohydride in the range of 20-100 mM. The sensitivities of the three perovskites towards borohydride oxidation indicated that LaCr0.4Ag0.6O3 is the best among all the perovskites studied giving a value of 1.395 𝜇A/mM.

    • Author Affiliations

       

      S Suresh Balaji1 A Usha1 V V Giridhar1

      1. Nano-Scale Electrocatalysis and Sensor Research Group, Electrodics and Electrocatalysis Division, CSIR-Central Electrochemical Research Institute, Karaikudi 630 006, India
    • Dates

       
  • Journal of Chemical Sciences | News

© 2021-2022 Indian Academy of Sciences, Bengaluru.