    • Keywords

       

      CdS; LB films; octadecylsuccinic acid; epitaxy

    • Abstract

       

      Cadmium sulphide (CdS) nanoparticles were grown by the reaction of sodium sulphide (Na2S) with Langmuir-Blodgett (LB) films of cadmium salts ofn-octadecylsuccinic acid (ODSU) and with LB films of ODSU in mixtures of octadecylamine and octadecyl alcohol. The results indicate that heterogeneous nucleation and aggregation in the pure ODSU LB films due to processes like Ostwald ripening are destabilized by the presence of the long-chain amine and alcohol in mixed systems. CdS nanoparticles in the LB films were monitored by UV-visible absorption spectra, which allow an estimation of the size of the particles. The morphology, size and nature of the nanocrystallites formed depend on whether the sulphidation was done on the pure film or in the mixed films. It is seen that particles of size around 1.6 nm were formed in ODSU/octadecylalcohol and ODSU/ octadecylamine mixed LB films while in pure ODSU films the size was about 2.7 nm. These films showed typical needle-shaped structures, as observed by the optical microscopic technique. Mean size and morphology were confirmed by transmission and scanning electron microscopy, while selective area electron diffraction patterns showed six-fold symmetry and indicated that the CdS crystals grow epitaxially with respect to the monolayer. Further, the crystallisation enhanced in the mixed LB films showed a characteristic zinc oxide (Wurtzite) structure compared with the pure ODSU matrix.

    • Author Affiliations

       

      G Hemakanthi1 Balachandran Unni Nair1 Aruna Dhathathreyan1

      1. Chemical Laboratory, Central Leather Research Institute, Adyar, Chennai - 600 020, India
    • Dates

       
  • Journal of Chemical Sciences | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.