      Magnetron sputtering; XRD; electrical conductivity; dielectric behaviour; Raman scattering.

    • Abstract

       

      The quest for low power consumption devices with new functionalities has made the negative capacitance (NC) effect, the most captivating and studied phenomenon. The NC effect is observed in Cu–TiC thin film at a low frequencyrange between 112.9 Hz and 2 kHz. The Cu–TiC thin film was deposited on Si (100) substrate by DC magnetron co-sputtering process and then annealed in a vacuum at different temperatures (100–600$^{\circ}$C). The magnitude ofNC increased from $-$0.016 to $-$27.5 lF after annealing. The NC behaviour is also observed in the forward biased region of the capacitance–voltage ($C–V$) characteristics. The current–voltage ($I–V$) characteristics reveal the decreasing static and dynamic resistance for higher annealed films. An improved electrical conductivity ($27.70 \times 10^3$ to $384.62 \times 10^3$ S m$^{-1}$)is evidenced with decreasing ideality factor (2.01–0.55) in the post-annealed films. The films were found to be polycrystalline from X-ray diffraction patterns with Cu and TiC phases. Raman studies have also confirmed the presence of Cuand TiC vibrational modes in all films. The intensity of C peaks detected at 1359 cm$^{-1}$ (D peak) and at 1590 cm$^{-1}$ (G peak) in the as-deposited film decreased after annealing. The annealing effect reduced the amount of unreacted carbon and contributed to form stoichiometric TiC from non-stoichiometric TiC.

    • Author Affiliations

       

      AVISHEK ROY1 2 ARUN KUMAR MUKHOPADHYAY1 3 MUKUL GUPTA4 ABHIJIT MAJUMDAR1

      1. Department of Physics, Indian Institute of Engineering Science and Technology, Shibpur, Howrah 711103, India
      2. Department of Electronics, Vidyasagar College, Kolkata 700006, India
      3. Department of Physics, Dinabandhu Andrews College, Kolkata 700084, India
      4. UGC-DAE Consortium for Scientific Research, Indore 452017, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.