• Effect of WO$_3$ nanoparticle doping on the physical properties of PVC polymer

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/043/0149

    • Keywords

       

      Poly(vinyl chloride); PVC/WO$_3$ polymer films; optical energy gap; urbach energy; dielectric constant; Cole–Cole.

    • Abstract

       

      Poly(vinyl chloride)/tungsten oxide (PVC/WO$_3$) nanocomposite films were synthesized with different ratio of WO$_3$ content (0, 0.05, 0.1, 0.2 and 0.3 wt%). The sol–gel method was used to prepare WO$_3$ nanoparticles (NPs). X-ray diffraction and scanning electron microscope techniques confirmed that the WO$_3$ NPs were successfully dispersed in a PVC matrix with a single-phase structure. Characteristic absorption bands were observed in infrared spectra for pure PVC and nanocomposites. The morphology of WO$_3$ was observed using transmission electron microscope. The optical energy band gaps ($E_{\rm opt}$; direct and indirect) were estimated by using Tauc’s formula. It was found that the direct band gap energies decreased from 5.15 to 4.53 eV and the indirect bands decreased from 4.8 to 4.1 eV as WO$_3$ doping increased, while the Urbach energy ($E_{\rm u}$) increased as WO$_3$ content increased. It was found that the steepness parameter decreased, which confirms the formation of localized states in the band gap and increasing disorder in PVC polymer samples. The dielectric constant ($\epsilon'$) of the PVC/WO$_3$ nanocomposite films decreased as frequency increased. At a low frequency region, the loss factor ($\epsilon''$) has a high value and then sharply decreased as frequency increased, reaching a frequency independent region at high frequency values. The obtained data are very useful for using the investigated samples (PVC/WO$_3$) as the cores of high frequency transformers with very low dielectric loss.

    • Author Affiliations

       

      A M A HENAISH1 2 A S ABOUHASWA3 4

      1. Physics Department, Faculty of Science, Tanta University, Tanta 31527, Egypt
      2. NANOTECH Center, Ural Federal University, Ekaterinburg 620002, Russia
      3. Physics Department, Faculty of Science, Menoufia University, Shebin Elkoom 32511, Menoufia, Egypt
      4. Institute of Natural Science and Mathematics, Ural Federal University, Yekaterinburg 620002, Russia
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.