• Effect of titanium oxide ceramic particles concentration on microstructure and corrosion behaviour of Ni–P–Al$_2$O$_3$–TiO$_2$ composite coating

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/043/0099

    • Keywords

       

      Composite coating; titanium oxide; corrosion; potentiodynamic polarization.

    • Abstract

       

      Composite coatings are coatings that have been considered in terms of properties, such as corrosion resistance, oxidation resistance and excellent hardness. In this study, Ni–P–Al$_2$O$_3$–TiO$_2$ composite coating was made on AISI 316 steel using direct current deposition technique. The microstructure of the coating and its corrosion resistance were studied bychanging the amount of titanium oxide (1, 2, 3 and 4 g l$^{−1}$) in the bath. To investigate the morphology of the coating and the analysis of the coated material, a scanning electron microscope (SEM) and EDS microscopy were conducted, respectively. The results showed that in the bath containing 4 g l$^{−1}$ titanium oxide, the coating is perfectly uniform and continuous, while by reducing the amount of titanium oxide, it is not possible to form a suitable coating on the entire surface of the substrate. To investigate the corrosion resistance, the potentiodynamic polarization and electrochemical impedance spectroscopy testsin aqueous solution of 3.5% NaCl were carried out on coated and uncoated samples. The results of these tests were also correlated with microscopic images and showed that the coatings in a bath containing 4 g l$^{−1}$ titanium oxide has the highest corrosion resistance.

    • Author Affiliations

       

      FARHAD MOHSENIFAR1 HADI EBRAHIMIFAR2

      1. Department of Mechanical Engineering, Higher Education Complex of Bam, Bam 7661314477, Iran
      2. Department of Materials Engineering, Faculty of Mechanical and Materials Engineering, Graduate University of Advanced Technology, Kerman 7631133131, Iran
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.