• Effect of different parameters on the tribological performance of polypropylene/thermoplastic polyurethane blends under dry sliding conditions

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/042/03/0092

    • Keywords

       

      Polymer blends; maleic anhydride-grafted polypropylene; abrasive wear; hardness.

    • Abstract

       

      In this study, polypropylene/thermoplastic polyurethane (PP/TPU) blends (weight ratios of 75/25 and 25/75) were produced by melt blending, and a maleic anhydride-grafted polypropylene (PP-g-MA) copolymer was used as a coupling agent. The effect of the concentration of the coupling agent (5–11 phr), TPU concentration (25–75%), normal load (2–4 N) and sliding velocity (60–72 rpm) on the wear properties of the blends were characterized through a pin-on-discabrasive wear test. A 2$4^$ full-factorial experimental design was chosen to screen the significant factors and their interactions influencing the tribological performance of the blends. After the tests, the morphology of the worn surface of the samples was observed using scanning electron microscopy. Shore D hardness tests were also conducted and the relationships between these behaviours were analysed on the basis of the findings. According to the wear test results, the factors that have the greatest effect on the wear rates are as follows: normal load, TPU concentration, sliding velocity and PP-g-MA concentration,respectively. The wear rate of the blends increases by increasing the normal load, TPU concentration and sliding speed, and slightly decreases by increasing the PP-g-MA concentration. As expected, the wear and hardness results showed the apparent superiority of the PP$_{75}$/TPU$_{25}$ blends over the PP$_{25}$/TPU$_{75}$ blends, because of the higher content of rigid segments in the blends.

    • Author Affiliations

       

      SONER SAVAS1

      1. Department of Materials Science and Engineering, Engineering Faculty, Erciyes University, 38039 Melikgazi, Kayseri, Turkey
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.