    • Keywords

       

      Jet electrodeposition; NiFeW alloy coating; current efficiency; microstructure; microhardness.

    • Abstract

       

      In this paper, ternary NiFeW alloy coatings were prepared by jet electrodeposition, and the effects of lord salt concentration, jet speed, current density and temperature on the properties of the coatings, including the composition, microhardness, surface morphology, structure and corrosion resistance, were investigated. Results reveal that the depositionrate reaches a maximum value of 27.30 $\mu$m h$^{−1}$, and the total current efficiency is above 85%. The maximum microhardness is 605 HV, and the wear and corrosion resistance values of the alloy coating are good. Moreover, the ternary NiFeW alloy coating is smooth and bright, and it presents a dense cellular growth. The alloy plating is nanocrystalline and has face-centered cubic structure.

    • Author Affiliations

       

      J K YU1 J ZHAO1 M Q YU2 H L LUO2 3 Q QIAO1 S ZHAI1 Z F XU2 KAZUHIRO MATSUGI2

      1. State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, People’s Republic of China
      2. Graduate School of Engineering, Hiroshima University, 1-4-1, Kagamiyama, Higashi-Hiroshima 739-8527, Japan
      3. Hebei Provincial Key Laboratory of Heavy Machinery Fluid Power Transmission and Control, Yanshan University, Qinhuangdao 066004, People’s Republic of China
    • Dates

       
  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.