• Fabrication of CdSe quantum dots/permutite luminescent materials

    • Fulltext


        Click here to view fulltext PDF

      Permanent link:

    • Keywords


      Nanocrystalline materials; composite materials; luminescence; permutite.

    • Abstract


      Permutite incorporating CdSe in mesopores has been prepared with a simple route. Firstly, mercaptosuccinic acid-capped CdSe quantum dots (QDs) were prepared in aqueous solution by using SeO2 as selenium source and NaBH4 as reductant. Secondly, the commercial permutite was treated with acetic acid to induce a partial dealumnization, which can introduce a large number of intracrystal mesopores, and the CdSe QDs were successfully incorporated in the mesopores with the wet impregnation method. Photoluminescence spectra, X-ray diffraction and scanning electron microscopy were used for the characterization of samples. The spectra analyses results showed that the illuminant colour of QDs/permutite powder was similar to the corresponding QDs colloid. X-ray diffraction measurements indicated that the (1 0 1) diffraction peak at 2𝜃 = 27° for QDs/permutite powder was the same as the raw permutite, and the energy-dispersive X-ray spectra demonstrated that Cd and Se elements existed in the CdSe QDs/permutite powder.

    • Author Affiliations


      Meihua Yu1 Yilin Wang1 2

      1. Ministry-Province Jointly-Constructed Cultivation Base for State Key Laboratory of Processing for Non-ferrous Metal and Featured Materials, Guangxi Zhuang Autonomous Region, Guangxi University, Nanning 530004, China
      2. School of Chemistry and Chemical Engineering, Guangxi University, Nanning 530004, China
    • Dates

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.