      Characterization; undercooling solidification; differential scanning calorimeter (DSC); flux processing technique; jet electrodeposition; Ni–W–P ternary alloy.

    • Abstract


      The undercooling of Ni–W– P ternary alloy coating melt was investigated by in situ differential scanning calorimeter (DSC) with the flux processing technique. The results showed that the highest undercooling of Ni–W–P ternary alloy with 359 K was obtained as the thermal treatment temperature of themelt being 1679 K and the cooling rate being 50 K min-1. When cooling rate is fixed, the change of undercooling depends on the melt processing temperature, and the undercooling will increase rapidly at the first stage. The effects of thermal treatment temperature and cooling rates on the undercooling were discussed.

    • Author Affiliations


      J K Yu1 Y H Wang1 G Z Xing1 Q Qiao1 B Liu1 Z J Chu1 C L Li1 F You1

      1. State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, Hebei, PR China
    • Dates

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.