    • Keywords

       

      Aluminides; nickel; zirconium; diffusion; CVD.

    • Abstract

       

      Influence of Zr on the microstructure and phase characteristics of aluminide diffusion coatings deposited on the nickel substrate has been investigated in this study. The coatings with and without zirconium were deposited by CVD method. The cross-section chemical composition investigations revealed that during the coatings formation, there is an inward aluminum diffusion and outward nickel diffusion in both types of coatings (with and without zirconium), whereas zirconium is located far below the coating surface, at a depth of ∼17 𝜇m, between 𝛽-NiAl phase and 𝛾'-Ni3Al phase. XRD examinations showed that 𝛽-NiAl, 𝛾-NiAl and 𝛾'-Ni3Al were the main components of the deposited coatings. 𝛽-NiAl phase is on the surface of the coatings, whereas 𝛾-NiAl and 𝛾'-Ni3Al form deeper parts of the coatings. Zirconium is dissolved in NiAl on the border between 𝛽-NiAl and 𝛾'-Ni3Al.

    • Author Affiliations

       

      Jolanta Romanowska1 Maryana Zagula-Yavorska1 Jan Sieniawski1

      1. Department of Materials Science, Rzeszów University of Technology, 2, W. Pola st, 35-958 Rzeszów, Poland
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.