• Changes in microstructural parameters of NB4D2 silk fibres due to electron irradiation: X-ray line profile analysis

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/034/07/1583-1590

    • Keywords

       

      Irradiation; microstructural parameters; WAXS, fibre.

    • Abstract

       

      The present study is concerned with changes of microcrystalline parameters in NB4D2 (Bombyx mori) silk fibres, due to electron irradiation. The irradiation process was performed in air at room temperature using 8 MeV electron beam at different dose rates: 0, 25, 50 and 75 kGy, respectively. X-ray recording of these irradiated samples and the line profile analysis were carried out. The crystal imperfection parameters such as crystallite size $\langle N \rangle$, lattice strain (g in %) and surface weighted crystallite size ($D_{s}$) were computed and compared with other physical parameters in order to asertain the changes that have crept into these irradiated fibres. Exponential, lognormal and Reinhold functions for the column length distributions have been used for the determination of these parameters.

    • Author Affiliations

       

      Sangappa1 S Asha1 P Parameswara2 R Somashekar2

      1. Department of Studies in Physics, Mangalore University, Mangalagangotri 574 199, India
      2. Department of Studies in Physics, University of Mysore, Manasagangotri, Mysore 570 006, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.