• Annealing twins in a multifunctional beta Ti–Nb–Ta–Zr–O alloy

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/034/07/1435-1438

    • Keywords

       

      Titanium alloy; annealing; EBSD; CSL; twinning.

    • Abstract

       

      The grain boundary character distribution and annealing twins in a multifunctional 𝛽-type Ti–23Nb–0.7Ta–2Zr–O alloy having a stable bcc phase structure are investigated by electron backscattering diffraction (EBSD). The results show that the coincident site lattice (CSL) boundaries, including 𝛴 3 and 𝛴 11 twin boundaries mainly form at the early stage of recrystallization. {112}$\langle$111$\rangle$ and {332} $\langle$113$\rangle$ annealing twins are observed to occur in the completely recrystallized Ti–23Nb–0.7Ta–2Zr–O alloy.

    • Author Affiliations

       

      W Y Guo1 J Sun2

      1. Shanghai Baosteel Packaging Co. Ltd, Shanghai 201908, P.R. China
      2. School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, P.R. China
    • Dates

       
  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.