      Ti3SiC2–SiC composites; hot pressing; reaction synthesis.

    • Abstract

       

      The microstructure and mechanical properties of Ti3SiC2–SiC nanocomposite fabricated by in situ hot pressing (HP) synthesis process were studied. The results show that dense Ti3SiC2–SiC composite contained minor TiSi2 obtained by hot sintering at 1350°C for 1 h. The average grain size of Ti3SiC2 was 4 𝜇m in length, and the size of SiC grains is about 100 nm. With its fine microstructure, the Ti3SiC2–SiC nanocomposite shows good mechanical properties.

    • Author Affiliations

       

      Baoyan Liang1 Mingzhi Wang2 Xiaopu Li2 Yunchao Mu1

      1. Materials and Chemical Engineering School, Zhongyuan University of Technology, Zhengzhou 450007, China
      2. Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, China
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.