• Synthesis and characterization of composites of mixed oxides of iron and neodymium in polymer matrix of aniline–formaldehyde

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/034/04/0843-0851

    • Keywords

       

      Nanocomposites; polymer matrix; neodymium oxide; spinel ferrites; quadrupole splitting; Scherrer equation.

    • Abstract

       

      Nanocomposites of mixed oxides of iron and neodymium in polymer matrix of anilineformaldehyde are reported. The composites have been obtained by treating the aqueous solution of aniline, hydrochloric acid and formaldehyde with halide of iron and neodymium oxide. The infra-red spectra show broad peaks at ∼ 590 cm-1 and at ∼ 610 cm-1 due to the presence of oxides of both iron and neodymium. In heated samples, the absorption peaks due to metal oxides are better resolved. A broad and strong peak in XRD spectra at 2𝜃 value of 35.69920 corresponds to spinel 𝛾-Fe2O3. 57Fe Mössbauer spectrum for unheated sample gives Mössbauer parameters, i.e. isomer shift (𝛿), quadrupole splitting (𝛥 𝐸) and effective magnetic field (Heff). Transmission electron microscopy (TEM) micrographs reveal well dispersed particles at different magnifications. Vibrating sample magnetometry (VSM) studies indicate that the ferrite nanoparticles exhibit characteristics of ferromagnetism.

    • Author Affiliations

       

      Sajdha1 H N Sheikh1 B L Kalsotra1 N Kumar2 S Kumar3

      1. Department of Chemistry, University of Jammu, Jammu 180 006, India
      2. Defence Laboratory, Jodhpur, India
      3. DRDO, New Delhi, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.