    • Abstract

       

      In this work, pH dependent evolution of tungsten oxide (WO3) nanostructures is being reported along with physical characteristics. The synthesis was carried out via an inexpensive solvothermal cum chemical reduction route, with sodium tungstate (Na2WO4) and cetyl trimethyl ammonium bromide (C19H42NBr) as main reactants. The X-ray diffraction, together with transmission electron microscopic studies have revealed formation of regular polyhedral nanocrystalline structures and fractals as one goes from higher pH (= 5.5) to lower pH (= 2) values. The average crystallite size, as calculated throughWilliamson–Hall plots, was varied within 2.8–6.8 nm for different pH samples. Fourier transform infrared spectroscopy reveals in-plane bending vibration 𝛿 (W–OH), observable at ∼1630 cm-1 and strong stretching 𝜈 (W–O–W) located at ∼814 cm-1. Raman spectroscopy has divulged WO3 Raman active optical phonon modes positioned at ∼717 and 805 cm-1. The thermochromic and photochromic properties of the nanoscale WO3 sample prepared at pH = 5.5, are also highlighted.

    • Author Affiliations

       

      Vijay Bhooshan Kumar1 Dambarudhar Mohanta1

      1. Nanoscience Laboratory, Department of Physics, Tezpur University, Tezpur 784 028, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.