    • Heat capacity measurements on Yb𝑥Gd2–𝑥Zr2O7 (𝑥 = 0, 1, 2) ceramics by differential scanning calorimetry

      Zhan-Guo Liu Jia-Hu Ouyang Yu Zhou

      Ceramics and Glasses Volume 32 Issue 6 December 2009 pp 603-606

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/032/06/0603-0606

    • Keywords

       

      Yb𝑥Gd2–𝑥Zr2O7; heat capacity; differential scanning calorimetry; enthalpy.

    • Abstract

       

      Yb𝑥Gd2–𝑥Zr2O7 (𝑥 = 0, 1, 2) ceramics were pressureless-sintered using ceramic powders acquired by chemical-coprecipitation and calcination methods. Heat capacities of Yb𝑥Gd2–𝑥Zr2O7 were measured with a heat flux-type differential scanning calorimetry in the temperature range of 298–1200 K. At 298 K, the heat capacities of Gd2Zr2O7, YbGdZr2O7 and Yb2Zr2O7 were 214, 221 and 230 J.K-1 mol-1, respectively.

    • Author Affiliations

       

      Zhan-Guo Liu1 Jia-Hu Ouyang1 Yu Zhou1

      1. Institute for Advanced Ceramics, Department of Materials Science, Harbin Institute of Technology, Harbin 150001, P R China

    • Dates

       
      Published
      December 2009
      Manuscript received
      23 July 2009

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.

Contact | Site index