• Carbon nanotube synthesis from propane decomposition on a pre-treated Ni overlayer

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/032/02/0135-0140

    • Keywords

       

      Carbon nanotubes; Ni-catalysed growth; APCVD; AFM; HRTEM; micro Raman spectroscopy.

    • Abstract

       

      Growth of carbon nanotubes (CNTs) was performed by atmospheric pressure chemical vapour deposition (APCVD) of propane on Si(111) with a pre-treated Ni overlayer acting as a catalyst. Prior to the growth of CNTs, a thin film of Ni was deposited on Si(111) substrate by evaporation and heat treated at 900°C. The growth of nanotubes was carried out at 850°C using propane as a source of carbon. Distribution of the catalyst particles over the Si substrate was analysed before and after heat treatment by atomic force microscopy (AFM). The X-ray diffraction (XRD) pattern of the grown material revealed that they are graphitic in nature. Field emission scanning electron microscopy (FESEM) was used to investigate the growth process and it was found that a catalytic particle was always situated at the tip of the tube thus implying a tip growth mechanism. Evidence for the presence of radial breathing mode from multi-wall nanotubes (MWNTs) in the grown sample was obtained from micro-Raman analysis. Finally, high-resolution transmission electron microscopic (HRTEM) analysis confirmed that the graphene layers of the CNTs are well ordered with typical 0.34 nm spacing.

    • Author Affiliations

       

      J Sengupta1 S K Panda1 C Jacob1

      1. Materials Science Centre, Indian Institute of Technology, Kharagpur 721 302, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.