• Investigations on d.c. conductivity behaviour of milled carbon fibre reinforced epoxy graded composites

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/031/04/0665-0668

    • Keywords

       

      Milled carbon; epoxy; gradient; d.c. conductivity.

    • Abstract

       

      This paper reports the d.c. conductivity behaviour of milled carbon fibre reinforced polysulphide modified epoxy gradient composites. Milled carbon fibre reinforced composites having 3 vol. % of milled carbon fibre and poly sulphide modified epoxy resin have been developed. D.C. conductivity measurements are conducted on the graded composites by using an Electrometer in the temperature range from 26°C to 150°C. D.C. conductivity increases with the increase of distance in the direction of centrifugal force, which shows the formation of graded structure with the composites. D.C. conductivity increases on increase of milled carbon fibre content from 0.45 to 1.66 vol.%. At 50°C, d.c. conductivity values were 1.85 × 10-11, 1.08 × 10-11 and 2.16 × 10-12 for samples 1, 2 and 3, respectively. The activation energy values for different composite samples 1, 2 and 3 are 0.489, 0.565 and 0.654 eV, respectively which shows decrease in activation energy with increase of fibre content.

    • Author Affiliations

       

      Navin Chand1 Archana Nigrawal1

      1. Advanced Materials and Processes Research Institute, Habibganj Naka, Bhopal 462 026, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.