1. Home
    2. Journals
    3. Bulletin of Materials Science
    4. Volume 31
    5. Issue 2

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/031/02/0189-0192

    • Keywords

       

      CuS nanoparticles; electrospinning; poly(vinyl alcohol).

    • Abstract

       

      Poly(vinyl alcohol) (PVA)/CuS composite nanofibres were successfully prepared by electrospinning technique and gas–solid reaction. Scanning electron microscopic (SEM) images showed that the average diameter of PVA/CuS fibres was about 150–200 nm. Transmission electron microscopy (TEM) proved that a majority of CuS nanoparticles with an average diameter of about 15–25 nm are incorporated in the PVA fibres. Xray diffraction (XRD) analyses and electron diffraction pattern also revealed the forming of CuS crystal structure in the PVA fibres.

    • Author Affiliations

       

      Jia Xu1 Xuejun Cui1 Jinhui Zhang1 Hongwei Liang2 Hongyan Wang1 Junfeng Li1

      1. College of Chemistry, Jilin University, Changchun 130012, People’s Republic of China
      2. State Key Laboratory of Inorganic Synthesis and Preparative, Jilin University, Changchun 130012, People’s Republic of China

    • Dates

       
      Published
      April 2008
      Manuscript received
      14 July 2007
      Manuscript revised
      19 January 2008

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.

Contact | Site index