• Possibilities of using welding-on technologies in crane wheel renovation

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/031/02/0125-0131

    • Keywords

       

      Traverse crane wheel; weld-on; weld-on wire; wearing.

    • Abstract

       

      The paper deals with analysis of welds-on quality of traverse crane wheels made from gr. 90–60 material, ASTM A148. Three types of welding-on technology with various filling materials were used. On wheel after wearing was welded-on one interlayer by a combination of additional materials, wire A 106 with F 11 addition and two cover layers made by a combination of A 508 wire with F 13 addition. Wheel surface was hardened after welding-on to a depth of 3 mm. A second welds-on technology was a combination of A 106 wire with F 11 addition. Two cover layers were made by a combination of RD 520 wire with F 56 addition. Third welds-on technology was realized to face one layer by C 113 wire in inert atmosphere: 80% Ar + 20% CO2. Two cover layers were made by wire with self protect Lincore 40-O. Properties of renovated traverse crane wheels were compared with the properties of new wheels with surface hardened layer. The welds-on were exposed to adhesive wearing where surface resistance was examined according to their weight loss. Influence of a particular element on the welds-on chemical composition was examined by EDX analyses.

    • Author Affiliations

       

      J Viňáš1 Ľ Kaščák1

      1. Department of Technology and Materials, Faculty of Mechanical Engineering, Technical University of Košice, Slovakia
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.