      Electrodeposition; electropolymerization; polynitroaniline; SEM studies; Zn–Ni alloy.

    • Abstract


      Electro-polymerization of orthonitroaniline was carried out on graphite electrode in hydrochloric acid medium. Zinc–nickel alloy deposition was carried out in the presence of polynitroaniline in acid sulphate bath. The bath constituent and bath variables were optimized through Hull cell experiments. The current efficiency and throwing power were measured. High shift of potential towards more cathodic direction was observed in presence of addition agent. Corrosion resistance test revealed good protection of base metal by zinc–nickel coating obtained from the developed electrolyte. SEM photomicrograph shows fine-grained deposit in the presence of addition agent. The consumption of brightener in the lab-scale was 0.01 gL-1 for 1000 amp-h.

    • Author Affiliations


      H P Sachin1 Ganesha Achary1 Y Arthoba Naik1 T V Venkatesha1

      1. Department of Chemistry, School of Chemical Sciences, Kuvempu University, Shankaraghatta 577 451, India
    • Dates

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2022-2023 Indian Academy of Sciences, Bengaluru.