      Metallic substrates; 𝛾-alumina; washcoat; Ce–Zr solid solution.

    • Abstract


      The influence of Ce0.68Zr0.32O2 solid solution on properties of 𝛾-alumina based washcoat on FeCrAl foils was investigated. FeCrAl foils were pretreated at 950°C in air for 10 h before coating washcoat. Different amounts of Ce0.68Zr0.32O2 solid solution were added into ã-alumina-based slurries. The properties of washcoats were measured by ultrasonic vibration and thermal shock test, SEM, BET and XRD. The results show that the addition of Ce0.68Zr0.32O2 solid solution into slurries can improve 𝛾-Al2O3-based washcoat adhesion on FeCrAl foils. The more the Ce0.68Zr0.32O2 solid solution added into slurries, the higher was the specific surface area of aged samples. XRD characterization proved that ceria–zirconia solid solution can inhibit the transformation of 𝛾-Al2O3 crystal into others at 1050°C for 20 h.

    • Author Affiliations


      Mei-Qing Shen1 2 Li-Wei Jia1 Wen-Long Zhou1 Jun Wang1 Ying Huang1

      1. Key Laboratory for Green Chemical Technology of State Education Ministry, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, P. R. China
      2. State Key Laboratory of Engines, Tianjin University, Tianjin 300072, P. R. China
    • Dates

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.