    • Keywords

       

      Mechanical properties; tribology performance; wear mechanism; POM/graphite/Ekonol composite.

    • Abstract

       

      POM/graphite/Ekonol composites were prepared by the Torque Rheometer mixing and compression molding, and their hardness, compressive and impact strengths have been tested. The tribology behaviour was also investigated by the friction and wear experiment. The worn surface of the composite was studied by SEM technique, and on its basis, the wear mechanism was analysed. Results show that it was possible to prepare POM/graphite/Ekonol composites of high tribology performance and good mechanical properties by the Torque Rheometer mixing and compression molding. With the rise of Ekonol content, the wear mechanism was changed from adhesion plus plough to fatigue wear plus abrasive wear.

    • Author Affiliations

       

      Chun-Guang Long1 Wen-Xian Liu1 Xia-Yu Wang1

      1. Department of Polymer Science and Engineering, Chemistry Institution, Xiangtan University, Xiangtan, Hunan 411200, P.R.China
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.