• An improved process for the synthesis of VPI-5 molecular sieve

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/026/03/0279-0281

    • Keywords

       

      VPI-5; synthesis; XRD; SEM; TG/DTA; FT-IR; MASNMR.

    • Abstract

       

      VPI-5 was synthesized with lesser time duration. The synthesized sample was characterized by XRD, SEM, FT-IR, TG/DTA, 27Al and 31P MASNMR techniques, which shows that the synthesized sample was highly crystalline. Carbon and nitrogen analyses reveal that the sample contains no template molecules, however, TG/DTA analysis shows the presence of physisorbed template molecules. MASNMR results show the presence of three different types of aluminium and phosphorous. Two of them were present as in tetrahedral and the remaining one is present in octahedral environment.

    • Author Affiliations

       

      N Venkatathri1

      1. Catalysis Division, National Chemical Laboratory, Pune 411 008, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.