• Mössbauer studies on athermal martensite formation in an Fe–Ni–Mn alloy

    • Fulltext


        Click here to view fulltext PDF

      Permanent link:

    • Keywords


      Austenite–martensite; Mössbauer spectroscopy; scanning electron microscopy; isomer shift.

    • Abstract


      In this study, austenite–martensite phase transformations which are formed by cooling effect in Fe–30% Ni–0.2% Mn alloy are investigated with Mössbauer spectroscopy and scanning electron microscopy. The single peak of the paramagnetic phase and the six peaks of the ferromagnetic phase of Fe–30% Ni–0.2% Mn alloy were observed in the Mössbauer spectrum. The internal magnetic field strength of ferromagnetic martensite phase was determined as 33.8 𝑇 and the isomer shift values were determined as – 0.11 mm.sec–1 and – 0.06 mm.sec–1, respectively, for the austenite and martensite phases. In this alloy, athermal transformation was observed. The results obtained are in agreement with literature.

    • Author Affiliations


      A Aydin1 E Guler1 H Aktas1 H Gungunes1

      1. Kirikkale University, Faculty of Art and Science, 71450 Kirikkale/Türkiye
    • Dates

  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.