    • Keywords

       

      Hot isostatic pressing (HIP); bismuth layered structure ferroelectrics (BLSF); ferroelectromagnetic materials; relaxor ferroelectrics

    • Abstract

       

      X-ray diffraction, a.c. impedance and conductivity (a.c. and d.c.) have been used to characterize DyBi5Fe2Ti3O18. Samples were prepared by solid state double sintering method. A few samples were also subjected to hot isostatic pressing (HIP) at 800°C for 2 h at 100 MPa pressure. The data on XRD, impedance and conductivity of two sets of samples are compared to understand study of effect of HIPing on the properties of DyBi5Fe2Ti3O18

    • Author Affiliations

       

      N V Prasad1 G Prasad1 Mahendra Kumar1 2 S V Suryanarayana1 T Bhimasankaram1 G S Kumar1

      1. Department of Physics, Osmania University, Hyderabad - 500 007, India
      2. Defence Metallurgical Research Laboratory, Hyderabad - 500 058, India

    • Dates

       
      Published
      December 2000
      Manuscript received
      9 May 2000
      Manuscript revised
      14 September 2000

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2022-2023 Indian Academy of Sciences, Bengaluru.

Contact | Site index