      Magnetization; Mg-Zn ferrites; sintering

    • Abstract


      Magnesium zinc ferrites with the general formula MgxZn(1 −x)Fe2O4 were prepared by the standard ceramic technology route involving double sintering. X-ray analysis was carried out to confirm the single-phase formation as well as to calculate the lattice parameters. Two sets of samples were prepared by sintering the samples at 1100°C for 15 and 30 h respectively. The high-field loop tracer was used to measure the hysteresis parameters. It is observed that the sintering conditions effectively modify the magnetization characteristics of these ferrites.

    • Author Affiliations


      S H Patil1 S I Patil1 S M Kadam1 S R Patil1 B K Chougule1

      1. Department of Physics, Shivaji University, Kolhapur - 416 004, India
    • Dates

  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.