• Electron microscopic studies of thermomechanically aged 2218 aluminium alloy

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/010/03/0217-0222

    • Keywords

       

      Thermoechanical ageing; 2218 Al alloy; transmission electron metallography; plastic deformation; precipitation; zone formation; dislocation; microstructure

    • Abstract

       

      The effect of thermomechanical ageing (TMA) treatment on the microstructure and mechanical properties of 2218 Al alloy has been studied. This was followed by hardness measurements and transmission electron metallography (TEM). The 2218 Al alloy was given various thermomechanical ageing treatments including partial peak ageing, warm rolling and further ageing to peak hardness level. Without thermomechanical treatment the peak hardness value was 130 VHN. With thermomechanical treatment there was an overall improvement in hardness. This is attributed to the combined effect of dislocation precipitate networks and the fineness ofθ′ particles.

    • Author Affiliations

       

      Mukesh Kumar1 S Singh1 D B Goel1

      1. Department of Metallurgical Engineering, University of Roorkee, Roorkee - 247 667, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Dr Shanti Swarup Bhatnagar for Science and Technology

      Posted on October 12, 2020

      Prof. Subi Jacob George — Jawaharlal Nehru Centre for Advanced Scientific Research, Jakkur, Bengaluru
      Chemical Sciences 2020

      Prof. Surajit Dhara — School of Physics, University of Hyderabad, Hyderabad
      Physical Sciences 2020

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2021-2022 Indian Academy of Sciences, Bengaluru.