      Microstructure; dielectric behaviour; glass ceramic; differential thermal analysis

    • Abstract

       

      Glasses in the system PbO-BaO-TiO2-B2O3-SiO2 with and without P2O5 as nucleant have been prepared. The glass samples were ceramized based ondta studies. The ferroelectric phase crystallizing out has been found to be BaTiO3 fromxrd. The optical and scanning electron micrographs show the presence of BaTiO3 as major phase. In these glass ceramic samples, dielectric constant and dissipation factor are approximately constant with temperature and frequency upto the glass transition temperatureTg and thereafter increase sharply with temperature and finally level off. The addition of P2O5 as nucleant and molar ratio of (PbO + BaO) to TiO2 has marked influence on the dielectric behaviour and composition of ferroelectric phase crystallizing out.

    • Author Affiliations

       

      OM Parkash1 Devendra Kumar1 2 R Rajgopalan1

      1. School of Materials Science and Technology, Banaras Hindu University, Varanasi - 221 005, India
      2. Department of Ceramic Engineering, Institute of Technology, Banaras Hindu University, Varanasi - 221 005, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.