• Magnetic properties of a mischmetal-cobalt alloy

    • Fulltext

       

        Click here to view fulltext PDF


      Permanent link:
      https://www.ias.ac.in/article/fulltext/boms/002/03/0177-0180

    • Keywords

       

      Solidification; atmosphere quenching

    • Abstract

       

      The magnetic properties of a mischmetal-cobalt alloy are studied. A mischmetal-64% cobalt alloy was melted in induction furnace under a protective atmosphere of argon. The melt was solidified in a magnetic field of 7 kOe, and cooled to a temperature of 950° C and was thereafter quenched in water. Specimens of suitable dimensions were machined, heat-treated in the temperature range 1000–1100° C for various lengths of time and the magnetic properties evaluated. The (BH)max value was 10·3 MGOe which was associated with aBr value of 7 kG and Hc value of 5 kOe. The results obtained offer feasibility to design new MM-Co5 magnets through developments in processing technique.

    • Author Affiliations

       

      R A Tewari1

      1. Metallurgy Division, Materials Science Centre, Indian Institute of Technology, Kharagpur - 721 302, India
    • Dates

       
  • Bulletin of Materials Science | News

    • Editorial Note on Continuous Article Publication

      Posted on July 25, 2019

      Click here for Editorial Note on CAP Mode

© 2017-2019 Indian Academy of Sciences, Bengaluru.